Autoclave vessel is an equipment gets physical mechanics from reaction to hydrate of silicate produce. Usage of the autoclave vessel is important to safety of producing and utilize of energy.
Main Technical Parameters:
|Max pressure||1.6 Mpa||1.6 Mpa||1.6 Mpa|
|Working pressure||1.5 Mpa||1.5 Mpa||1.5 Mpa|
|Workingmedium||Saturated steam||Saturated steam||Saturated steam|
1.50000m3-300000m3 Sand AAC Production Line
Areated concrete brick (light brick ) is the light and porous buidling material. It has
light keeping temperature cant burn and other advantages. It can be made into many
kindsof bricks (for example: 600X200X100, 80X80X180, 240X115X53, 600X200X125 ),
theycould be used industry building and common building. They are more and more popular in the world. In the future, they will replace the Clay brick completely.
2. 50000m3-300000m3 Sand AAC Production Line
Common concrete density is usually 1600-2400kg/m3, but Areated concrete are
500kg/m3, 600kg/m3, 700kg/m3. Main use silicon material (for example: Coal ash,
sand, Stone dust and others ), through making the material small for example sand,
they can be Used directly if has enough degree of small (for example coal ash. Mixing calcium material Lime cement water to a special slop, then add the aluminum dust and
the additive. Make the Aluminum dust and the special slop have a Chemical reflect. Then produce Hydrogen to make The concrete slop to expanding or swell, foam. Next, put them into the curing room to Concreting cutting steaming curing, last, there will bacome the
light brick, the porous rate Is 70-80%.
3. 50000m3-300000m3 Sand AAC Production Line
1). Light weight
Areated concrete density is usually 400-700kg/m3, (according the market in produce ), same as 1/3 of clay brick and 1/5 common concrete. So use the Light brick can reduce
the weight ofThe build more, and also reduce the beam of roof and pillar press best.
Then you can see, it Can save the material and cost, it also fighting shaking.
2). Keeping temperature
It has many are porous, the delivery hearting coefficient is 0.9-0.22W/(mk), the same as
1/4 Or 1/5 of clay brick, so it is best materials now in the world.
4. 50000m3-300000m3 Sand AAC Production Line
AAC block machine plant, light weight block machine, aerated concrete block machine,
AAC brick machine line, light weight brick machine, aerated concrete brick machine, autoclaved aerated concrete block machine.
1). Product weight is according to 600kg/m3 to control.
2). Annual capacity 200, 000M3.
3). Set raw material proportion: Cement 6.5%, raw lime 23%, flyash 68%, gypsum 3%, aluminum Paste powder 350G/M3.
4). Water and material rate 0.631
5). One mould product 2.88M3
6). Casting slurry cycle time 5-6 minutes, cut cycle time 5 minutes.
7). Casting slurry temperature 38-42 degree
8). Body quiet stop. Time is 1.5-2.5housr, temperature 50-90 degree, after quiet stop
body Strength is 0.15-0.18MPa
9). Steam curing cycle time, come in and out autoclave about 0.5hour, steam curing
cycle time About is 6 hours/1.6MPa, total 6.5 hours.